The mechanical properties of individual multi-wall boron nitride nanotubes (MWBNNTs) synthesized by a growth-vapor-trapping chemical vapor deposition method are investigated by a three-point bending technique via atomic force microscopy. Multiple locations on suspended tubes are probed in order to determine the boundary conditions of the supported tube ends. The bending moduli (EB) calculated for 20 tubes with diameters ranging from 18 to 58 nm confirm the exceptional mechanical properties of MWBNNTs, with an average EB of 760 ± 30 GPa. For the first time, the bending moduli of MWBNNTs are observed to increase with decreasing diameter, ranging from 100 ± 20 GPa to as high as 1800 ± 300 GPa. This diameter dependence is evaluated by Timoshenko beam theory. The Young’s modulus and shear modulus were determined to be 1800 ± 300 and 7 ± 1 GPa, respectively, for a trimmed data set of 16 tubes. The low shear modulus of MWBNNTs is the reason for the detected diameter-dependent bending modulus and is likely due to the presence of interwall shearing between the crystalline and faceted helical nanotube structures of MWBNNTs.

Very Stable Electron Field Emission from Strontium Titanate Coated Carbon Nanotube Matrices with Low Emission Thresholds

June 18, 2017 Renato Pinto Reveggino

FE-matrices-ACS-Nano2013

Novel PMMASTOCNT matrices were created by opened-tip vertically aligned multiwalled carbon nanotubes (VAMWCNTs) with conformal coatings of strontium titanate (STO) and poly(methyl methacrylate) (PMMA). Emission threshold of 0.8 V/μm was demonstrated, about 5-fold lower than that of the as-grown VA- MWCNTs. This was obtained after considering the related band structures under the perspective of work functions and tunneling width as a function of the STO thickness. We showed that there is an optimum thickness of STO coatings to effectively reduce the work function of CNTs and yet minimize the tunneling width for electron emissions. Furthermore, simulation and modeling suggest that PMMASTOCNT matrices have suppressed screening effects and Coulombs’ repulsion forces between electrons in adjacent CNTs, leading to low emission threshold, high emission density, and prolonged emission stability. These findings are important for practical application of VA-MWCNTs in field emission devices, X-ray generation, and wave amplification.